3201 PA-F Nylon
Characteristics
Technology: SLS (Selective Laser Sintering)
Build Time: 72h (Big size parts or bulk / high volume orders will be longer)
Color: Grayish Black
Tolerance: ±0.3mm (Within 100mm), ±0.4% (Above 100mm)
Recommended Wall Thickness: 1.0mm
Max Build Size: 350 x 350 x 400mm
Min Build Size: 5mm x 5mm x 5mm / 10mm x 2mm x 2mm
Heat Deflection Temperature: 147°C
Mechanical Properties
| Measurement | Test Method | Value |
| Heat deflection temperature | ASTM D648 @0.45 MPa | 147°C |
| Flexural strength | ASTM D790 | 49MPa |
| Flexural modulus | ASTM D790 | 1,300MPa |
| Impact strength notched Izod | ASTM D256 | 6.0 KJ/m² |
| Hardness Shore D | ASTM D2240 | 74 |
| Tensile modulus | ASTM D638 | 1,500 MPa |
| Tensile strength | ASTM D638 | 44 MPa |
| Elongation at break | ASTM D638 | 35% |
Features
Good Toughness: 3201 PA-F Nylon provides excellent toughness, making it suitable for parts that need to withstand impact and stress without breaking.
Excellent Mechanical Properties: This material offers high tensile strength (44 MPa) and a moderate flexural modulus (1300 MPa), ensuring that parts are strong and durable.
Good Printing Accuracy: With a high level of precision, this material is ideal for detailed and intricate designs.
Grain Surface Textures: The SLS process typically results in parts with a grainy and textured surface, which can be advantageous for certain applications where texture is desirable or additional grip is needed.
Suitable for High-Performance Parts: Due to its robust properties, 3201 PA-F Nylon is well-suited for creating parts that require high performance and reliability.